Ceramic-Ceramic Articulation Surface Implants

ABSTRACT

A prosthesis for articulation (e.g., hip or joint prosthesis) is provided, which includes a pair of articulation components respectively defining a pair of articulation surfaces movably engageable with each other. In some embodiments, each of the articulation surfaces is formed from a biocompatible ceramic (e.g., doped silicon nitride ceramic) having a flexural strength greater than about 700 Mega-Pascal (MPa) and a toughness greater than about 7 Mega-Pascal root meter (MPam 0.5 ).

CROSS-REFERENCE TO RELATED APPLICATIONS

This application is a continuation of U.S. application Ser. No. 10/987,415, filed on Nov. 12, 2004, which is a divisional of U.S. application Ser. No. 10/171,376, filed Jun. 13, 2002, now U.S. Pat. No. 6,881,229, which claims priority to U.S. Provisional Appln. 60/298,669, filed Jun. 14, 2001, all of which are hereby incorporated by reference herein in their entireties.

BACKGROUND OF THE INVENTION

This invention relates generally to improvements in articulating joint prostheses, particularly such as an improved prosthetic hip joint or the like. More specifically, this invention relates to a combination of an improved ceramic material articulating against a well known and established metal for use in a metal-ceramic composite articulation which exhibits long wear characteristics with substantial elimination of wear debris, and which further exhibits reduced in-vivo fracture risk. Additionally, this invention is also related to the ability to use metal femoral heads with ceramic acetabular liners. The specific clinical benefits of this feature stem from the ability to use fracture resistant heads with low wear and substantial wear debris elimination, the use of large head diameters, which greatly facilitates minimizing risk of dislocation of the head from the prosthetic joint, and providing surgeons and patients with the choice of using this combination for revision of failed joint prostheses.

Typical articulating joints, which consist of a metal surface articulating with a ultra-high molecular weight polyethylene (PE) are inadequate. Clinical studies have shown that the principal cause of implant failure is osteolysis secondary to wear of the implant bearing-surfaces. The primary cause appears to be particulate debris in the form of ultra-high molecular weight polyethylene (PE) released, for example, from the PE acetabular liner bearing of a hip prosthesis¹. Such PE wear debris when released into the peri-implant tissues appears to elicit a deleterious biologic reaction, incorporating foreign-body giant cell and macrophage cell responses leading to bone resorption, and eventual loosening of the prosthetic implant. As a consequence, alternative rigid-on-rigid bearing materials such as ceramic-on-ceramic (C-C) (such as alumina), metal-on-metal (M-M), and the recent cobalt chrome alloy (CoCr)—heavily cross linked PE (XPE) are being introduced.

Clinical experience from 1983 to the present has encompassed over two million alumina ceramic femoral-head implants.^(2, 3) Total hip replacement studies incorporating both CoCr and alumina ceramic heads have established the superiority of ceramic-PE couples over metal-PE couples, with alumina-alumina couples demonstrating 2-3 orders lower wear volume than the best ceramic-PE couples.⁴ Even so, the major limitation to use of alumina ceramics today is the likelihood of brittle fracture, even in just a low incidence of 2% or less. From the limited series of clinical studies available in the United States, the failure incidence of alumina heads was found to be surprisingly high and of quite short follow-up periods, anywhere from 9 months to 10 years.”^(6, 5) Thus the fracture incidence in ceramics is still of clinical concern. Typical ceramic materials have low toughness and are prone to failure by brittle fracture. As history has indicated, there is an urgent need to find an improvement to alumina, particularly with ceramic-ceramic couples which have higher bearing contact stresses.⁶

Low wear of articulating components occurs when the mating surfaces have comparable and high hardness, good surface finish, conformal surface geometry, compatible mechanical properties and a low coefficient of friction. It is because of the first three conditions that ceramic-ceramic couples have demonstrated very low wear. Contact damage results in the weaker material when the moduli and hardness of the articulating surfaces are very different, as is the case for CoCr-PE or even zirconia or alumina ceramic-PE. An ideal articulating low wear couple will have closely matching properties and high toughness. Traditional ceramics such as alumina are prone to brittle fracture owing to their low toughness. Such brittle failure in ceramic materials results from propagation of microcracks initiated at and just below the surface. Other ceramic materials such as zirconia, zirconia toughened alumina or Si₃N₄ that have higher toughness have significantly higher reliability than alumina, owing to the ability to avoid catastrophic failure. Specifically, using such ceramics can allow significant improvements in wear properties along with improved reliability. The specific advantages can be illustrated by considering the articulating hip joint. If the articulating hip joint can be made with a metal femoral head and a ceramic acetabular cup, additional significant clinical benefits can be obtained as listed below:

-   -   The metal femoral head does not fail catastrophically as ceramic         heads can, assuring patient safety;     -   The metal head can be made of a larger size, up to 44 mm         diameter, than ceramic heads can typically be made, providing         the surgeon greater flexibility in implant size selection; and     -   The metal head can be used as both a primary hip prosthesis or a         revision hip prosthesis.

This invention describes a Si₃N₄ acetabular cup-CoCr femoral head couple. This couple is superior to other ceramic-metal couples such as alumina-metal,^(7, 8, 9) owing to compatible properties such as hardness, tensile strength, elastic modulus, high fracture toughness, and lubricity. Si₃N₄ also has an optimal combination of toughness and strength properties that gives superior damage resistance: the ability to retain strength following contact damage. Friction property studies of Si₃N₄ ceramics show that Si₃N₄-(M-50) steel hybrid bearings and Si₃N₄—Si₃N₄ bearings had the lowest friction coefficients under both lubricated and dry conditions of the materials tested. In contrast, alumina ceramic-ceramic and alumina-steel bearings had approximately three times the friction coefficient when tested under similar conditions.

It is therefore an object of this invention to provide a new set of bio-compatible articulating surface materials for use in prosthetic joints which will have:

-   -   Ultra-low wear with volumetric wear rates of less than 1 mm³/10         million cycles;     -   Long in-vivo life;     -   Wide range of sizes maximizing surgeon choice and optimizing fit         to patient anatomy;     -   Wide bio-mechanical margin of safety for all sizes, minimizing         risk of in-vivo fracture;     -   Preserving modularity of prosthetic articulating joint designs;         and     -   Allowing both primary and revision prosthetic articulating joint         designs.

SUMMARY OF THE INVENTION

In accordance with the invention, an improved joint prosthesis such as a hip, knee or shoulder joint or the like is provided with articulation between a first component and a second component, wherein at least one of these joint components is formed from a selected ceramic material designed for high fracture toughness or resistance, and further wherein the assembled joint components are designed for long-term articulation with minimal wear and resultant minimal production of undesired wear debris. The first component has an articulation surface formed from a bio-compatible ceramic with enhanced flexural strength and toughness properties, and wear properties compatible with the second component which has an articulation surface formed from a bio-compatible ceramic with enhanced flexural strength and toughness properties, or from a metallic alloy.

For example, in one embodiment, an implantable articulating bone prosthesis (e.g., hip or joint prosthesis) is provided, which includes a pair of articulation components respectively defining a pair of articulation surfaces movably engageable with each other. In some embodiments, each of the articulation surfaces is formed from a biocompatible ceramic (e.g., doped silicon nitride ceramic) having a flexural strength greater than about 700 Mega-Pascal (MPa) and a toughness greater than about 7 Mega-Pascal root meter (MPam^(0.5)).

In a preferred form, the first component of the articulatory prosthesis is formed from a silicon nitride ceramic material doped with other oxides such as yttrium oxide and alumina. Other dopants can include magnesium oxide, or strontium oxide.

Other features and advantages of the invention will become more apparent from the following detailed description taken in conjunction with the accompanying drawings which illustrate, by way of example, the principles of the invention.

BRIEF DESCRIPTION OF THE DRAWINGS

The accompanying drawings illustrate the invention. In such drawings;

FIG. 1 is a graph illustrating the results of three point bend testing for Si₃N₄ ceramic test samples;

FIG. 2 is a graph illustrating the fracture toughness of the Si₃N₄ ceramic test samples depicted in FIG. 1;

FIG. 3 is a graph showing wear test results for simulated hip prostheses using Si₃N₄ ceramic acetabular cup and femoral heads (Si₃N₄ ceramic-Si₃N₄ ceramic, Stations 1 and 2), and a Si₃N₄ ceramic acetabular cup and CoCr metal femoral head (Si₃N₄ ceramic-metal, Station 3); and

FIG. 4 is a graph showing wear performance of Si₃N₄ ceramic acetabular cup and ceramic femoral head components (Si₃N₄ ceramic-Si₃N₄ ceramic), and Si₃N₄ ceramic cup and metal (Si₃N₄ ceramic-metal) head hip prostheses through an extended wear cycle, in comparison with metal-to-metal and traditional ceramic-to-ceramic in-vitro wear data.

DETAILED DESCRIPTION OF THE PREFERRED EMBODIMENTS

Powders of Si₃N₄ and dopants such as alumina, yttria, magnesium oxide, and strontium oxide were conventionally processed to form a doped composition of silicon nitride. The dopant amount was optimized to achieve the highest density and mechanical properties. The homogeneous powders were then cold isostatic pressed at 300 Mega-Pascal (MPa) followed by sintering in a controlled atmosphere. Some cold isostatically pressed bars were hot isostatically pressed. A sintering temperature of 1875° C. was found optimal to achieve high density, absence of pores and other flaws and a uniform fine-grained microstructure. The best combination of density and mechanical properties was achieved with Si₃N₄ doped with 6 weight % Y₂O₃+4 weight % Al₂O₃.

Flexural strength was measured on standard 3-point bend specimens per American Society for Testing of Metals (ASTM) protocol method C-1161 and fracture toughness measured using single edge notched beam specimens per ASTM protocol method E399. Bend tests were conducted using test fixtures designed to minimize spurious stresses, with a nominal span of 40 mm. The bending load was applied using a universal testing machine at a cross-head displacement speed of 0.5 mm/min. At least 6 bars were tested to get a measure of the distributions and the Weibull modulus. The composition/process that gave the highest fracture toughness, Weibull modulus and damage resistance was selected for fabricating 28 mm hip prosthesis implant articular femoral head and acetabular cup components. 28 mm CoCr metal femoral heads were obtained from Biomet, Inc. of Warsaw, Ind.

Wear performance tests of up to 1 million cycle duration were conducted. Wear detection was primarily done gravimetrically with some inspection of the surfaces for wear track analysis and wear debris analysis using scanning electron microscopy. In the hip prosthesis simulator test, the rotating cams (uni-directional) carrying the specimen chambers were driven at 1 Hz frequency through +23° arcs on orthogonal axes. Each vertical load column had a self alignment device and friction torque sensors. In addition, both the anti-rotation peg and the friction sensor pegs were guide mounted on rollers to provide continuous constraint. For this study, the cam rotation was synchronized with the hip-joint loading. The “Paul” physiologic load profile was used.^(10, 11) All tests were run at 2 KiloNewton (kN) peak load/0.2 kN minimum load. The test cups were arranged in an anatomically inverted position in the hip prosthesis simulator. A solution of 90% bovine serum was used as the lubricant with 10% standard additives of sodium azide and ethylene diamine tetra-acetic acid (EDTA). The specimen chambers were replenished with distilled water during the tests. Lubricant temperature was monitored but not controlled since the lubricant's bulk temperatures run in the range 36-40° C., close to body temperature. The ceramic cups were not sterilized prior to test. Soak control cups were not used for the ceramic-ceramic and ceramic-metal wear tests. The diametral clearance, surface finish and sphericity tolerance was noted. Component wear was determined using a gravimetric method. Wear components were cleaned and dehydrated and each set weighed four times in order with a 32 mm CoCr head as a calibration standard. The overall volumetric wear rate was determined by the slope of the linear regression line. A consistent wear rate, i.e. gradient of the linear regression trend was deemed more significant than the actual magnitude of the wear at any point in time.

Microstructural features such as grain size, pore size, porosity and defects were observed on sintered Si₃N₄ specimens after etching with carbon tetra-fluoride plasma. The specimens were found to be dense, with no detectable porosity, and had substantially uniform grain size consistent with high quality ceramics.

For fracture toughness testing, 2.5 mm×5 mm×25 mm bar specimens with varying notch depth, a, were prepared. The prepared specimens were tested in three-point bending with a span length of 20 mm. The resultant fracture loads were converted to fracture toughness values using ASTM protocol method E399. The fracture strength and toughness values are given in Table 1, and are plotted in FIGS. 1 and 2. As expected, hot iso-statically pressed specimens labeled as SNH and SNH-1 exhibited high strength, toughness and Weibull moduli. Hence hot iso-static pressed components were fabricated into acetabular and femoral components. The relevant mechanical characterization data obtained are tabulated in Table 1.

TABLE 1 Weibull Modulus and Characteristic Fracture Strength of Si₃N₄. Weibull Modulus Characteristic Strength Fracture Toughness Material M σ_(f) (MPa) K_(lc) (MPam^(0.5)) SNH 34.9 853 9.10 (0.66) SNH-1 19.1 952 9.61 (0.95)

The results indicate that SNH and SNH-1 have a substantially optimized high flexural strength, greater than about 900 MPa, and fracture toughness, greater than about 9 MPam^(0.5).

A trial wear test using a hip simulator was conducted using Si₃N₄ acetabular cups articulating against Biomet's standard 28 mm CoCr metal femoral heads (previously identified). Three Biomet 28 mm heads were used. The mating Si₃N₄ acetabular ceramic cups were ground without lapping. The surface roughness value (R_(B)) value was ˜0.5 μm. High wear of the metal femoral heads was observed, attributed to the higher surface roughness, which resulted in scouring the surface of the CoCr metal femoral heads. The wear behavior was found to be linear and typical of 3-body wear, dominated by unstable characteristics. The lubricant solution exhibited the concomitant amount of CoCr metal debris. Further, the wear tracks showed non-polar contact rather than polar contact as anticipated from the low diametral clearance. Fine scratch marks and wear tracks were observed midway between the pole and equator, while the pole had a shiny sheen, indicative of equatorial contact.

For subsequent wear tests, the Si₃N₄ acetabular and femoral components were ground and lapped to obtain an R_(B)<0.05 μm. The diametral clearance and sphericity was also varied. The CoCr metal femoral heads were made from a wrought high carbon CoCr alloy containing about 64 weight % cobalt, about 28% weight chromium, about 6% weight molybdenum, about 0.5% weight manganese, about 0.25% weight iron, about 0.2% weight nickel, about 0.2% weight nitrogen and about 0.23% weight carbon. The conventional low carbon CoCr alloy had a similar elemental weight composition with a carbon content of about 0.06% by weight. Such CoCr alloys used for joint prostheses are wrought alloys conforming to ASTM Specification 1537, This high carbon alloy had an elastic modulus greater than 210 giga Pascal (GPa), which had a closer modulus match to the doped Si₃N₄ ceramic (elastic modulus ˜300 GPa) compared to the low carbon CoCr alloy used in the trial run. The Vickers hardness of these alloys is in the range of 4-5 GPa compared to between 14-16 GPa Si₃N₄. The elastic modulus and hardness of the articulating surfaces of the doped Si₃N₄ ceramic-Si₃N₄ ceramic or the doped Si₃N₄ ceramic-CoCr alloy pair are better matched compared to either CoCr-PE, or CoCr-XPE articulations. This was expected to result in better wear performance.

Relevant design data pertaining to the articulating femoral head and acetabular cup pairs chosen for the wear study are tabulated in Table 2. Stations 1 and 2 had Si₃N₄ ceramic acetabular cup-Si₃N₄ ceramic femoral head bearings, and Station 3 had a Si₃N₄ ceramic acetabular cup-CoCr metal femoral head bearing. For the Si₃N₄ ceramic-Si₃N₄ ceramic bearings in Stations 1 and 2, a 70 and 100 μm diametral clearance was chosen to test the effect of run-in wear. The sphericity tolerance of the ceramic acetabular cups was between 1-1.5 μm in all cases and was less than 0.5 μm for both the ceramic femoral heads. For the Si₃N₄ acetabular cup-CoCr femoral head bearing, a diametral clearance of about 200 μm was selected.

TABLE 2 Design Tolerances for the Second Wear Performance Test. Surface Diameter Roughness, Sphericity Components (mm) R_(a) (μm) (μm) Station 1 Ceramic Cup 28.0734 0.0390 1.486 Ceramic Head #4 27.9704 0.0440 0.419 Diametral Clearance  103 μm Station 2 Ceramic Cup 28.0552 0.0074 1.448 Ceramic Head #2 27.9856 0.0447 0.851 Diametral Clearance 69.6 μm Station 3 Ceramic Cup 28.0252 0.0091 1.041 CoCr Head 743650 C 27.7986 0.0149 3.785 Diametral Clearance 226.6 μm 

The results from the wear test are plotted in FIG. 3. Stations 1 and 3 with diametral clearance of about 100 and 225 μm showed ultra low wear, with no observable run-in wear. In contrast, Station 2 with a low diametral clearance of about 70 μm showed classic biphasic behavior as is typical for metal-metal and ceramic-ceramic bearings. This biphasic behavior is attributed to the lower diametral clearance which, owing to inadequate film lubrication between the articulating surfaces, results in run-in wear.

Comparing the wear performance of the silicon nitride ceramic-ceramic bearings in Stations 1 and 2, it was noted that the bearing in Station 2 exhibited a “grinding” noise along with an increase in lubricant temperature during the run-in period. Following the run-in period, both Stations 1 and 2 behaved normally, with very low steady state wear rates. This was attributed to the lower diametral clearance used in Station 2, which may have resulted in an inadequate lubricant film to be developed between the femoral head and acetabular cup. The wear performance of the Si₃N₄ acetabular ceramic cup-CoCr metal femoral head bearing was characterized by an absence of run-in wear, similar to that of Station 1, and very low steady state wear rates. This result was as anticipated where, with better modulus matching, a ceramic-metal articulation couple could provide a ultra-low wear alternative for total hip arthroplasty.

The wear performance of these bearings was obtained over a 4 million cycle period. The weight loss data obtained were converted to volumetric wear rates and extrapolated to 10 million cycles to enable a comparison to literature values. The data, plotted in FIG. 4, indicate that the Si₃N₄ femoral head-Si₃N₄ acetabular cup bearings and the Si₃N₄ acetabular cup-CoCr metal femoral head show ultra-low wear of 0.65 mm³/10 million cycles and 3.4 mm³/10 million cycles respectively. In comparison, wear rates of 62 mm³/10 million cycles for CoCr-PE (clinical data), 6.5 mm³/10 million cycles for metal-metal (in-vitro) wear and 0.35-0.6 mm³/10 million cycles for alumina ceramic-alumina ceramic (in-vitro) have been reported.

Observation of the articulating components after 1 million cycles of wear testing, validated the ultra-low wear behavior by exhibiting a complete absence of wear tracks or other wear patterns. The articulating surfaces retained their high shine, consistent with the negligible weight loss observed for the components.

The above-described optimized material properties of Si₃N₄ have demonstrated a 100% increase of fracture toughness over alumina, and a 50% increase in fracture strength over alumina ceramics, which typically have a fracture toughness of about 5 MPam^(0.5) and a flexural strength of about 600 MPa, These properties of Si₃N₄ can allow the manufacture of total hip arthroplasty implants and other prosthetic joint implants such as knee and shoulder joints with significantly higher safety and reliability. Wear performance of Si₃N₄ femoral head-Si₃N₄ acetabular cup components and Si₃N₄ acetabular cup-CoCr femoral head components indicates that these bearings are better than metal-metal bearings and comparable to ceramic-ceramic bearings, with a volumetric wear rate of 2 orders of magnitude lower than CoCr-PE and 20 times lower than CoCr-XPE bearings.

The combination of the metal femoral head and a ceramic acetabular cup described above offers unprecedented benefits owing to inherent fracture resistance and excellent wear performance. The fracture resistance is derived from the use of metal femoral heads instead of ceramic femoral heads. It is well known from finite element analyses of the stresses in hip prosthetic joints that the femoral head component is subjected to high tensile stresses. Historically, such tensile stresses have been implicated in ceramic head fracture. Metal femoral heads do not fracture owing to the ductile nature of metals. Hence use of metal heads avoids fracture risk, In contrast, the acetabular cup component is typically subjected mainly to compressive stresses, which ceramics are designed to withstand. Furthermore, the combination of high toughness and flexural strength provides improved capability to withstand loads. Thus, as a general design principle for articulating prosthetic joints, the articulating component subjected to the higher tensile stresses can be made from a metal and the mating articulating component subjected to the higher compressive stresses can be made from the high strength high toughness ceramic with favorable tribiological properties. To illustrate this by way of example, in the hip joint, the femoral head can be made of metal and the mating acetabular cup can be made of the ceramic. In the case of knee joints, the condylar component which is subjected to higher tensile stresses, can be made from metal while the mating tibial component can be made from the ceramic. Similarly, the concept can be extended to other articulating prosthetic joints such as the shoulder joint.

The use of Si₃N₄ femoral head-Si₃N₄ acetabular cup components and Si₃N₄ acetabular cup-CoCr femoral head components in the instant invention to demonstrate the concept of using a fracture resistant metal alloy articulating with optimized ceramics to obtain an ultra low wear joint are illustrative of the general concept. Alternate metal alloys suitable for medical implants such as zirconium based alloys, titanium based alloys or stainless steel alloys may be used for the femoral head of a hip joint (or the component subjected to higher tensile stresses). Alternate enhanced toughness ceramic materials such as doped zirconia or zirconia toughened alumina could also be used for the acetabular component of a hip joint (or the component subjected to higher compressive stresses). This concept can also be applied to other orthopedic joints such as the shoulder or knee joint.

A variety of further modifications and improvements in and to the invention will be apparent to those persons skilled in the art. Accordingly, no limitation on the invention is intended by way of the foregoing description and accompanying drawings, except as set forth in the appended claims.

LITERATURE CITED

-   1. Callaway G. H., Flynn W., Ranawat C. S., and Sculco T. P., J.     Arthroplasty, 10, No. 6:855-859, 1995. -   2. Willman G., Pfaff H. G., and Richter H. G., Sonder. aus BioMed.     Technik, 40, 12, pp. 342-346, 1995. -   3. Clarke I. C. and Gustafson A., 6^(th) Biomat. Symp. Implant     Matls. In Orthop. Surg., ed. H. Willert and G. Buchorn, Gottingen     University, Germany, in press, 1995. -   4. Clarke I. C. and Gustafson A., In Press, Intl. Ceramics Congress,     Otsu City, Japan, November 1997. -   5. Mangione, P. Pascarel, X., Vinciguerra B, and Honton J. L., Intl,     Orthop., 18, pp. 359-362, 1994. -   6. Holmer P. and Nielsen P. T., J. Arthrop., 8, 567, 1993. -   7. B. Bhushan and L. B. Sibley, “Silicon Nitride Rolling Bearings     for Extreme Operating Conditions”, ASME Trans. 25, 4, pp. 417-428,     1981. -   8. D. L. Allen, “Effect of Composition and Physical Properties of     Silicon Nitride on Rolling Wear and Fatigue Performance”, Tribology     trans., Vol. 37, 2, pp. 410-414, 1994. -   9. J. W. Lucek, “Rolling Wear of Silicon Nitride Bearing Materials”,     ASME Gas Turbine and Aeroengine Congress and Expo., Brussels,     Belgium, 1990. -   10. Clarke I C, McKellop H A, Okuda R, McGuire P, Young R, and Hull     D, “Materials and prosthesis design criteria—hip simulator studies”,     Trans. 28th Ann. ORS, New Orleans, pp. 292, 1982. -   11. McKellop H and Clarke I. C., “Degradation and wear of Ultra-High     Molecular-Weight Polyethylene” In American Society for Testing &     Materials, ASTM STP 859:351-368, 1985. 

1. A prosthesis for articulation, comprising: a first component having a first ceramic articulation surface; and a second component having a second ceramic articulation surface for articulation with the first ceramic articulation surface, wherein at least one of the first ceramic articulation surface and the second ceramic articulation surface comprises biocompatible doped silicon nitride ceramic having a flexural strength greater than about 700 Mega-Pascal (MPa) and a toughness greater than about 7 Mega-Pascal root meter (Mpam^(0.5)).
 2. The prosthesis of claim 1 wherein the biocompatible doped silicon nitride ceramic has a toughness greater than about 9 Mega-Pascal root meter (Mpam^(0.5)).
 3. The prosthesis of claim 1 wherein each of the first ceramic articulation surface and the second ceramic articulation surface comprises a biocompatible ceramic having a flexural strength greater than about 700 Mega-Pascal (MPa) and a toughness greater than about 7 Mega-Pascal root meter (Mpam^(0.5)).
 4. The prosthesis of claim 1, wherein at least a portion of the first ceramic articulation surface is generally concave.
 5. The prosthesis of claim 4, wherein at least a portion of the second ceramic articulation surface is generally convex.
 6. The prosthesis of claim 1, wherein the biocompatible doped silicon nitride ceramic comprises aluminum oxide.
 7. The prosthesis of claim 1, wherein the biocompatible doped silicon nitride ceramic comprises yttria.
 8. The prosthesis of claim 1, wherein the biocompatible doped silicon nitride ceramic comprises aluminum oxide and yttria.
 9. The prosthesis of claim 1 wherein the biocompatible doped silicon nitride ceramic does not include strontium oxide.
 10. The prosthesis of claim 1 wherein each of the first component and the second component consists essentially of the doped silicon nitride ceramic.
 11. The prosthesis of claim 1, wherein the prosthesis comprises a hip joint prosthesis.
 12. The prosthesis of claim 1, wherein the prosthesis comprises a knee joint prosthesis.
 13. The prosthesis of claim 1, wherein the prosthesis comprises a shoulder joint prosthesis.
 14. A prosthesis for articulation, comprising: a first component having a first ceramic articulation surface; and a second component having a second ceramic articulation surface for articulation with the first ceramic articulation surface, wherein at least one of the first ceramic articulation surface and the second ceramic articulation surface comprises biocompatible doped silicon nitride ceramic.
 15. The prosthesis of claim 14, wherein the biocompatible doped silicon nitride ceramic comprises aluminum oxide.
 16. The prosthesis of claim 14, wherein the biocompatible doped silicon nitride ceramic comprises yttria.
 17. The prosthesis of claim 14, wherein the biocompatible doped silicon nitride ceramic comprises aluminum oxide and yttria.
 18. The prosthesis of claim 14 wherein the biocompatible doped silicon nitride ceramic does not include strontium oxide.
 19. The prosthesis of claim 14 wherein each of the first component and the second component consists essentially of the doped silicon nitride ceramic.
 20. The prosthesis of claim 14, wherein at least a portion of the first ceramic articulation surface is generally concave and wherein at least a portion of the second ceramic articulation surface is generally convex. 